标题：Structure and Solidification Process Observation of Fe-C-Cr Alloy Using Confocal Laser Scanning Microscope
本地全文：下载
作者：Shin Ito ; Hideki Kawai ; Yoshihiko Oishi 等
期刊名称：MATEC Web of Conferences
电子版ISSN：2261-236X
出版年度：2021
卷号：333
页码：1-6
DOI：10.1051/matecconf/202133311001
语种：English
出版社：EDP Sciences
摘要：In this study, we investigated the growth process of M7C3 carbide by a Confocal Laser Scanning Microscope. Fe-C-Cr alloy was prepared using an arc furnace. The composition was determined to be Fe:C:Cr=55:5:40(wt%). From the results of XRD and EPMA, the Fe-C-Cr alloy contained M7C3carbide in the internal structure. In condition of two cooling rates 60°C/min and 30°C/min observed with a Confocal Laser Scanning Microscope. Corners of the Hexagonal structure grew in the preferred orientation direction of M7C3carbide at 60°C/min. After the growth of preferred orientation direction, the M7C3carbide formed to connect between the corners. At a cooling rate of 30°C/min, M7C3carbides grew in oblique direction to the observation area. At the beginning, the structures were hidden in the fluid. But the structures started to grow, the shape of the hexagon became eventually. After the melting experiment, the samples were observed by Optical Microscope and Scanning Electron Microscope. As a result, since hexagonal structure arose a difference in height between the outside and the inside. M7C3 carbides grew from the outside in the solidification process.